Abstract
The latent properties and cure kinetics of an acid anhydride-cured epoxy resin have been investigated by a near-infrared (NIR) reflection spectroscopy. The assignments of the latent properties and cure behaviors were performed by the measurements of the NIR reflectance for epoxide and hydroxyl groups at different temperatures. A comprehensive analysis of the origin, location, and shifts during reaction of all major NIR absorption peaks in the spectral range from 4000 to 7100 cm-1 was provided. The extent of reaction was determined from NIR absorption band at the 4530 cm-1 depending on epoxide concentration and cure temperature.