Abstract
The thermal characteristics of epoxy resin (diglycidyl ether of bisphenol A, DGEBA, YD-128) containing 1, 2, 3wt% of thermo-latent initiator, N-benzylpyrazinium hexafluoroantimonate (BPH), were investigated. The specimens were stored at 300 °C in oxidation conditions for 0, 2, 4, and 8 hours. The flexural properties and fracture surface of the DGEBA/BPH system showed an optimum value at about 2∼3 wt% of BPH. The result of activation energy for thermal degradation in oxidation conditions showed that internal structure of DGEBA/BPH systems was stabilized as the retention time was increased. The similar result was also shown in flexural behavior. These results could be explained by the post-reaction of unreacted functional groups in the cured specimens by post-curing.
| Original language | English |
|---|---|
| Pages (from-to) | 435-445 |
| Number of pages | 11 |
| Journal | Polymer (Korea) |
| Volume | 22 |
| Issue number | 3 |
| Publication status | Published - 1 Dec 1998 |
| Externally published | Yes |
Keywords
- Activation energy
- DGEBA
- Flexural properties
- N-benzylpyrazinium hexafluoroantimonate (BPH)
- Post-curing
Fingerprint
Dive into the research topics of 'Thermal characteristics of thermo-latent initiator/epoxy cure systems in oxidation conditions'. Together they form a unique fingerprint.Cite this
- APA
- Author
- BIBTEX
- Harvard
- Standard
- RIS
- Vancouver