One-pot synthetic method to prepare highly N-doped nanoporous carbons for CO₂ adsorption

A one-pot synthetic method was used for the preparation of nanoporous carbon containing nitrogen from polypyrrole (PPY) using NaOH as the activated agent. The activation process was carried out under set conditions (NaOH/PPY = 2 and NaOH/PPY = 4) at different temperatures in 600-900 C for 2 h. The effect of the activation conditions on the pore structure, surface functional groups and CO₂ adsorption capacities of the prepared N-doped activated carbons was examined. The carbon was analyzed by X-ray photoelectron spectroscopy (XPS), N2/77 K full isotherms, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The CO₂ adsorption capacity of the N-doped activated carbon was measured at 298 K and 1 bar. By dissolving the activation agents, the N-doped activated carbon exhibited high specific surface areas (755-2169 m² g^-1) and high pore volumes (0.394-1.591 cm³ g^-1). In addition, the N-doped activated carbons contained a high N content at lower activation temperatures (7.05 wt.%). The N-doped activated carbons showed a very high CO₂ adsorption capacity of 177 mg g^-1 at 298 K and 1 bar. The CO₂ adsorption capacity was found to be dependent on the microporosity and N contents.